Material Overview: Rigid Resin is a photopolymer resin designed for Form 2 3D printers, reinforced with glass to provide high stiffness and a polished finish. It is suitable for printing thin walls and features, supporting print resolutions of 100 and 50 microns, and requires a Resin Tank LT.

Specifications:

Tensile Properties: Ultimate tensile strength is 40 MPa (green) and 75 MPa (post-cured). Tensile modulus is 2.2 GPa (green) and 4.1 GPa (post-cured). Elongation is 13.3% (green) and 5.6% (post-cured).
Flexural Properties: Flexural stress at 5% strain is 49 MPa (green) and 121 MPa (post-cured). Flexural modulus is 1.37 GPa (green) and 3.7 GPa (post-cured).
Impact Properties: Notched IZOD impact strength is 18.8 J/m (post-cured).
Temperature Properties: Heat deflection temperature at 1.8 MPa is 74°C, and at 0.45 MPa is 88°C. Thermal expansion is 53 μm/m/°C.

Solvent Compatibility: The material shows varying degrees of weight gain when immersed in different solvents for 24 hours. Notable values include 3.27% weight gain in Acetone and 5.34% in Strong Acid (HCI Conc).

Notes: Material properties can vary based on part geometry, print orientation, print settings, and temperature. Data was obtained from parts printed using Form 2 at 100 μm with Rigid settings, both in green and post-cured states.

Catalog excerpts

MATERIAL DATA SHEET Rigid Photopolymer Resin for Form 2 Rigid Resin is reinforced with glass to offer very high stiffness and a polished finish. This material is highly resistant to deformation over time and is great for printing thin walls and features. Supports print resolutions: 100 and 50 microns. Requires Resin Tank LT. To the best of our knowledge the information contained herein is accurate. However, Formlabs, Inc. makes no warranty, expressed or implied, regarding the accuracy of these results to be obtained from the use thereof.

Open the catalog to page 1

1 Material properties can vary with part geometry, print orientation, print settings, and temperature. 2 Data was obtained from green parts, printed using Form 2, 100 pm, Rigid settings, without additional treatments. 2 Data was obtained from parts printed using Form 2, 100 pm, Rigid settings and post-cured with a Formcure for 120 minutes at 80 C. FORMLABS MATERIAL PROPERTIES - RIGID: Photopolymer Resin for Form 2 3D Printers

Open the catalog to page 2

Rigid

Rigid

Catalog excerpts

All Formlabs catalogs and technical brochures