YOUR SPECIALIST FOR BRILLIANT RESULTS WITH HIGH-PERFORMANCE ZIRCONIUM DIOXIDE

Welcome to our world! We didn’t invent zirconium dioxide, but we have drastically optimized it! pritidenta – always one step ahead of the future. All ceramics date back more than 100 years; an American dentist invented the vry first porcelain jacket crown in 1900. The technique became popular in Europe in the 1920s despite being more complicated and problematic to fit. At the end of the 1980s, the advent of CAD/CAM technology in dentistry laid the foundations for the standard use of all ceramics. Today there is a wide range of available materials available. Zirconium dioxide offers the user the...

05 Let there be Light 07 Overview of product portfolio 10 priti®multidisc ZrO2 multicolor High Translucent 11 priti®multidisc ZrO2 multicolor Extra Translucent 12 priti®multidisc ZrO2 multicolor Translucent 13 The multicolor technology concept 16 priti®multidisc ZrO2 monochrome High Translucent 17 priti®multidisc ZrO2 monochrome Extra Translucent 18 priti®multidisc ZrO2 monochrome Translucent 19 priti®multidisc ZrO2 monochrome Opaque 20 priti®multibloc ZrO2 multicolor High Translucent

That's the way to do it!priti®multidisc ZrO2 and priti®multibloc ZrO2 Zirconium dioxide materials priti®multidisc ZrO2 J Can aU be sintered together at 1,450°C. * Any programmable furnace is suitable provided it is designed for high temperature sintering (up to 1,600°C). * Rapid sintering (up to 3-pontic bridges) is possible. * Precise rims and edges due to highly compacted material. * Any stain or glaze approved for zirconium dioxide can be used. J With or without gradation, has a diameter of 98.5 mm, making it suitable for all open milling machines. j Cross-batch color fidelity and homogeneous...

For our circular blanks we have developed four transLucency Levels with graduated transparency * priti®multidisc ZrO2 High Translucent with a transLucency of 49% * priti®multidisc ZrO2 Extra Translucent with a transLucency of 45% * priti®multidisc ZrO2 Translucent with a transLucency of 40% * priti®multidisc ZrO2 Opaque with a transLucency of 35% Extra Translucent High Translucent priti®multidisc ZrO2 multicolor priti®multidisc ZrO2 multicolor priti®multidisc ZrO2 multicolor Translucent Extra Translucent High Translucent 16 VITA® coLors A1-D4 16 VITA® coLors A1-D4 16 VITA® coLors...

Production workflow How are zirconium dioxide circular blanks produced? Manufactured at our in-house production site. Starting material Zirconium dioxide powder Every batch of powder is measured is recorded and traceable Shaping process Isostatic compression Shaping process controlled logged and documented Every blank is measured Compression of the green compact has its shrinkage measured and calculated is recorded and traceable Debonding White firing Quality control Pre-firing density Shrinkage Labeling

Overview of product portfolio priti®multidisc ZrO2 multicolor Extra Translucent High Translucent 49% translucency Flexural strength > 650 MPa Crowns and bridges with up to 3 pontics multicolor (4 light variants, 3 dark variants, 1 bleach shade) 45% translucency Flexural strength > 1,150 MPa Broad range of indications multicolor (4 light variants, 3 dark variants, 1 bleach shade) 40% translucency Flexural strength > 1,150 MPa Broad range of indications multicolor (4 light variants, 3 dark variants) Why does pritidenta offer so many different translucencies, colors and heights? Every lab or milling...

priti®multidisc ZrO2 multicolor High Translucent, Extra Translucent and Translucent Highly esthetic Harmoniously adjusted color gradients that meet the highest esthetic requirements. This means that fully anatomical restorations can be produced without ceramic veneering. Quick Without the otherwise standard and time-consuming work steps such as immersion, painting and drying, the sintering process can begin immediately after milling. Simple Simply by glazing and polishing you get impressive, highly esthetic, and brilliant results.

Color map pritidenta® Shade A light B light C light Positioning the restoration in an 18 mm A light blank produces a harmonious color gradient with colors A1, A2 or A3. Each multicolor shade covers a defined color range within its color gradient. Control the basic shade of your restoration by its position on the round blank. If the restoration is positioned centrally in a shade A light blank, the basic shade corresponds to A2. Closer to the top it becomes lighter, i.e. an A1, closer to the bottom it becomes darker, i.e. an A3. The positioning and color mapping can be adjusted to the right blank...

priti®muLtidisc ZrO2 muLticoLor High Translucent (5Y-TZP) 49% translucency, flexural strength > 650 MPa all open milling machines that accept round blanks with a diameter of 98.5 mm. The positioning and color mapping can be adjusted to the right blank height depending on the restoration height: Indications You can use priti®multidisc ZrO2 multicolor High Translucent to fabricate inlays, onlays, veneers, partial crowns, anatomically reduced and monolithic, fully anatomical crowns and bridges of up to three pontics for anterior and posterior areas. The translucency is comparable to that of lithium...

priti®multidisc ZrO2 multicolor Extra Translucent (4Y-TZP) 45% translucency, flexural strength > 1,150 MPa Indications You can use priti®multidisc ZrO2 Extra Translucent to fabricate anterior and posterior custom restorations on natural abutment teeth and implants. Zirconium dioxide Type II, Class 5 (DIN EN ISO 6872) Very high esthetics Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area Precise edges and margins due to highly compacted material Veneering possible with any ceramic mapped to the CTE of ZrO2 all open milling machines...