NON-PRECIOUS METAL MILLING DISCS (NPM)
2Pages

Milling disc made of grade 5 „ELI“ (Extra Low Interstitial) titanium alloy TiAl6V4. Milling disc made of pure titanium (Grade 4) with increased oxygen content. Composition in percent by mass Ti: 89.4 % Al: 6.2 % V: 4 % N, C, H, Fe, O: <0.4 % ADVANTAGES FOR DENTAL TECHNICIANS: Ű deal mechanical properties, manufactured according to ISO 5832-3 Ű Excellent bonding with ceramics for titanium Ű Biocompatible and corrosion-resistant Ű Particularly patient friendly due to low thermal conductivity Ű Perfect suitable for implant-supported restorations, superstructures, bars TECHNICAL PROPERTIES: Proof stress (Rp0.2) 837 MPa Ultimate tensile strength 921 MPa Elongation 15 % Vickers hardness 330HV5/30 VERSION 8 mm x 98.3 mm 10 mm x 98.3 mm 12 mm x 98.3 mm 13.5 mm x 98.3 mm 15 mm x 98.3 mm 16 mm x 98.3 mm 18 mm x 98.3 mm 25 mm x 98.3 mm 30 mm x 98.3 mm 8 mm x 99.5 mm 10 mm x 99.5 mm 12 mm x 99.5 mm 14 mm x 99.5 mm 15 mm x 99.5 mm 16 mm x 99.5 mm 18 mm x 99.5 mm 25 mm x 99.5 mm 30 mm x 99.5 mm Density Schmelzpunkt CTE (20-600 °C) Type (DIN EN ISO 22674) with edge without edge Composition in percent by mass Ti: >99 % N, C, H, Fe, O: <1 % ADVANTAGES FOR DENTAL TECHNICIANS: Ű Ideal for example for the production superstructures, bars and partial dentures Ű Perfect milling results Ű Excellent bonding with ceramics for titanium Ű Biocompatible and corrosion-resistant Ű Particularly patient friendly due to low thermal conductivity TECHNICAL PROPERTIES: Proof stress (Rp0.2) 504 MPa Ultimate tensile strength 599 MPa Elongation 23.5 % Vickers hardness >200 HV5/30 VERSION 8 mm x 98.3 mm 10 mm x 98.3 mm 12 mm x 98.3 mm 13.5 mm x 98.3 mm 15 mm x 98.3 mm 16 mm x 98.3 mm 18 mm x 98.3 mm 25 mm x 98.3 mm 30 mm x 98.3 mm 8 mm x 99.5 mm 10 mm x 99.5 mm 12 mm x 99.5 mm 14 mm x 99.5 mm 15 mm x 99.5 mm 16 mm x 99.5 mm 18 mm x 99.5 mm 25 mm x 99.5 mm 30 mm x 99.5 mm Density Schmelzpunkt CTE (20-600 °C) Type (DIN EN ISO 22674) with edge without edge NON-PRECIOUS METAL MILLING DISCS (NPM) Dental alloys already proven in conventional dental technology are also available as milling blanks. The same alloy components and compositions with excellent processing properties allows the user to work in one alloying system. NON-PRECIOUS METAL MILLING DISCS (NPM) S&S Scheftner GmbH Dekan-Laist-Straße 52 55129 Mainz / Germany E-Mail: service@scheftner.dental online:

COCR MILLING DISCS STARBOND EASY DISC STARBOND COS DISC BASIC CoCrW milling disc outstanding for manufacturing of crowns, bridges, frameworks, telescopes, bars, attachments, implant-supported superstructures. Starbond Easy Disc is based on a proven veneering alloy already used in conventional casting technique. CoCrMo milling disc with excellent properties for the manufacture of crowns, bridges, frameworks, telescopes, bars, attachments, implant supported superstructures. MoguCera C Disc is based on a non-precious ceramic alloy already used in the conventional casting technology. CoCrWMo...