NPM-PARTIAL DENTURE ALLOYS
2Pages

CoCr partial denture alloy for the whole range of removable partial dentures from combined fixed-removables restorations to clasp-retained dentures. Ű Ű Ű Ű Ű Ű TECHNICAL PROPERTIES: Proof stress (Rp0.2) Ultimate tensile strength Elongation Elastic modulus Vickers hardness Density Melting range Preheating temperature Casting temperature Laser weldable Type (DIN EN ISO 22674) Free of nickel, beryllium, cadmium and lead Type 5 according DIN EN ISO 22674 High degree of purity Biocompatible and corrosion-resistant High wearing comfort due to low thermal conductivity Composition: Co: 62.7 % Cr: 29 % Mo: 6 % C, Fe, Si, Mn: <1 % ADVANTAGES FOR DENTAL TECHNICIANS: Ű Excellent for casting of 3D printed plastic parts Ű System-free working due to very good alloy properties Ű Universally applicable for clasp-retained prostheses and combined techniques Ű Pleasant polishing properties and easy finishing Ű Optimal conditions for laser welding Ű Application flexibility and easy melting, no sparking NON-PRECIOUS METAL ALLOYS (NPM) NPM-PARTIAL DENTURE ALLOYS CoCr partial denture alloy for challenging combined restorations. Ű Ű Ű Ű Ű Ű Ű TECHNICAL PROPERTIES: Proof stress (Rp0.2) Ultimate tensile strength Elongation Elastic modulus Vickers hardness Density Melting range Preheating temperature Casting temperature Laser weldable Type (DIN EN ISO 22674) TECHNICAL PROPERTIES: Proof stress (Rp0.2) Ultimate tensile strength Elongation Elastic modulus Vickers hardness Density Melting range Preheating temperature Casting temperature CTE (25 - 600 °C) Laser weldable Type (DIN EN ISO 22674) Free of nickel, beryllium, cadmium and lead Type 5 according DIN EN ISO 22674 High degree of purity Biocompatible and corrosion-resistant High wearing comfort due to low thermal conductivity Spring-hard Composition: Co: 62 % Cr: 25 % W: 9 % Nb: 2 % C, V, Mo, Mn, Si: < 1 % ADVANTAGES FOR DENTAL TECHNICIANS: Ű Particularly suitable for extremely graceful removables Ű Ideal alloy for restorations which are exposed to very high loads Ű Excellent for casting of 3D printed plastic parts Ű Universally applicable for clasp-retained prostheses and combined techniques Ű Pleasant polishing properties and easy finishing Ű Optimal conditions for laser welding Ű System-free working due to very good alloy properties CoCr partial denture alloy (bondable) for challenging combined restorations and gracile clasp design. All-in-One diamonded polishing paste for metals, ceramics, zirconia, composites, plastics and acryllics. Free of nickel, beryllium, cadmium and lead Type 5 according DIN EN ISO 22674 High degree of purity Biocompatible and corrosion-resistant High wearing comfort due to low thermal conductivity Spring-hard Composition: Co: 62 % Cr: 30 % Mo: 5.5 % Si: 1 % C, Fe, Mn: <1 % NON-PRECIOUS METAL ALLOYS (NPM) Very high diamond content Hard paste consistency, thereby more efficient dosing No splashing or smearing - clean and economical Not suitable for intraoral use! Our non-precious metal alloys are characterized by excellent oral resistance and outstanding mechanical properties. Different compositions guarantee all restoration indications. Whether veneering with ceramic and acrylics, model casting and superstructures, our alloys produce highly aesthetic and natural results in excellent quality. ADVANTAGES FOR DENTAL TECHNICIANS: Ű Universally applicable for clasp-retained prostheses, combined techniques and ceramic restorations Ű Excellent for casting of 3D printed plastic parts Ű System-free working due to very good alloy properties Ű Pleasant polishing properties and easy finishing Ű Optimal conditions for laser welding Ű Application flexibility and easy melting, no sparking Rev. EN-09 / 2023-03 NON-PRECIOUS METAL ALLOYS (NPM) NPM-PARTIAL DENTURE ALLOYS S&S Scheftner GmbH Dekan-Laist-Straße 52 55129 Mainz / Germany

TECHNICAL PROPERTIES: Proof stress (Rp0.2) Ultimate tensile strength Elongation Elastic modulus Vickers hardness Density Melting range Preheating temperature Casting temperature CTE (25 - 600 °C) Laser weldable Type (DIN EN ISO 22674) CoCrMo bonding alloy for conventional, high-fusing (low expansion) ceramics. Free of nickel, lead, beryllium and cadmium Type 5 according to DIN EN ISO 22674 High degree of purity Biocompatible and corrosion-resistant Composition: Co: 59 % Cr: 25 % W: 9.5 % Mo: 3.5 % Si: 1 % C, Fe, Mn, N: <1 % ADVANTAGES FOR DENTAL TECHNICIANS: Ű Wide range of indications Ű...