Monolithic zirconia structure Slightly reduced zirconia structure FRESCO CERAMICS APPLICATION

TEST STRUCTURE: Minimal Cutback 0.3 – 0.7 mm FRESCO ENAMEL LUMINESCENCE VALUE OVERVIEW FRESCO ENAMEL FLUO/CONTROL UV LAMP KEAD4501 Fresco Enamel Fluo is used to recreate the natural restoration with a slightly translucent and luminous effect. In order to create different degrees of FRESCO ENAMEL TRANSPA 3 KEAD2301 Fresco Enamel Transpa 3 is a whitish luminous ceramic paste which increases the brightness and opacity of the zirconia structure. other Fresco pastes. FRESCO ENAMEL OPAL KEAD4601 Fresco Enamel Opal provides the restoration with a beautiful opalescent effect and recreates a natural luminous...

NOTE: for monolithic structures. FRESCO FIRING WORKFLOW FOR LAYERING MONOLITHIC SINGLE CROWNS AND SMALL BRIDGES SINTERED – MONOLITHIC CHARACHTERISED WITH ICE STAINS 3D BY ENRICO STEGER FRESCO ENAMEL FLUO/ CONTROL UNDER UV LAMP FINAL RESULT TIP: Perform a Fresco Firing n. 2 to maintain the modelled surface Fresco Firing n. 2. GLAZE AND STAIN FIRING OPTIONAL: GLAZE AND STAIN FIRING Heating rate Heating rate Heating rate Vacuum start Vacuum start Vacuum start OPTIONAL TIP: the surface can be further characterised or polished and/or can be carried out without loss in structure. TEXTURE OF A MONOLITHIC...

FRESCO FIRING WORKFLOW FOR LAYERING SLIGHTLY REDUCED SINGLE CROWNS AND SMALL BRIDGES SINTERED – SLIGHTLY REDUCED FRESCO ENAMEL FLUO/ CONTROL UNDER UV LAMP CHARACHTERISED WITH ICE STAINS 3D BY ENRICO STEGER APPLICATION OF FRESCO ENAMEL FINAL RESULT ICE Stains 3D by Enrico Steger FRESCO FIRING n. 1 GLAZE AND STAIN FIRING OPTIONAL: GLAZE AND STAIN FIRING Heating rate Heating rate Heating rate Heating rate Vacuum start Vacuum start Vacuum start Vacuum start

FRESCO FIRING WORKFLOW FOR LAYERING MONOLITHIC OR SLIGHTLY REDUCED PRETTAU® BRIDGES SINTERED – MONOLITHIC BEFORE FRESCO FIRING n. 1 AFTER FRESCO FIRING n. 1 CHARACHTERISED WITH ICE STAINS 3D BY ENRICO STEGER BEFORE FRESCO FIRING n. 2 GLAZE AND STAIN FIRING AFTER FRESCO FIRING n. 2 AFTER FRESCO FIRING n. 2 AFTER OPTIONAL GLAZE AND STAIN FIRING OPTIONAL: GLAZE AND STAIN FIRING Heating rate Heating rate Heating rate Heating rate Vacuum start Vacuum start Vacuum start Vacuum start Long-term cooling Long-term cooling Long-term cooling

FRESCO GINGIVA VS. NATURAL GINGIVA FRESCO GINGIVA 1 KEAD6301